Makrolon® FR6019 CTI

More Views

Makrolon® FR6019 CTI

Polycarbonate; flame retardant; MVR (300 °C/1.2 kg) 13 cm³/10 min; medium viscosity; UL 94V-0/1.5 mm; CTI = 600 V

Injection molding; High voltage application such as electric vehicles and battery packaging;

Thermal properties

Property	Test Condition	Value	Unit	Standard
Temperature of Deflection under Load (HDT)	0.45 MPa	125	°C	ISO 75-1,-2
Temperature of Deflection under Load (HDT)	1.80 MPa	112	°C	ISO 75-1,-2
Vicat Softening Temperature	50 N; 50 °C/h	130	°C	ISO 306
Coefficient of Linear Thermal Expansion (CLTE), parallel	23 to 55 °C	0.7	10⁻⁴/K	ISO 11359-1,-2
Coefficient of Linear Thermal Expansion (CLTE), normal	23 to 55 °C	0.71	10⁻⁴/K	ISO 11359-1,-2
Burning Behavior	1.5 mm	V-0		UL 94
Resistance to Heat (Ball Pressure Test)		120	°C	IEC 60695-10-2
Glow Wire Test (GWFI)	3.0 mm	960	°C	IEC 60695-2-12

Mô tả sản phẩm
Bình luận

Property	Test Condition	Value	Unit	Standard
Melt Volume-flow Rate (MVR)	300 °C/ 1.2 kg	13	cm³/10 min	ISO 1133-1
Molding Shrinkage, parallel	60x60x2 mm/ 500 bar	0.50 - 0.60	%	ISO 294-4
Molding Shrinkage, normal	60x60x2 mm/ 500 bar	0.50 - 0.60	%	ISO 294-4
Melt Viscosity	1000 s^-1^/ 300 °C	200	Pa·s	b.o. ISO 11443-A

Property	Test Condition	Value	Unit	Standard
Tensile Modulus	1 mm/min	2,470	MPa	ISO 527-1,-2
Yield Stress	5 mm/min	66	MPa	ISO 527-1,-2
Yield Strain	5 mm/min	6	%	ISO 527-1,-2
Nominal Strain at Break	5 mm/min	> 50	%	ISO 527-1,-2
Strain at Break	5 mm/min	119	%	ISO 527-1,-2
Stress at Break	5 mm/min	66	MPa	ISO 527-1,-2
Flexural Modulus	2 mm/min	2,450	MPa	ISO 178
Flexural Strength	2 mm/min	99	MPa	ISO 178
Flexural Strain at Flexural Strength	2 mm/min	7	%	ISO 178
Flexural Stress at 3.5 % Flexural Strain	2 mm/min	76	MPa	ISO 178
Izod Notched Impact Strength	23 °C	9	kJ/m²	ISO 21305/based on ISO 180/A
Charpy Notched Impact Strength	23 °C	11	kJ/m²	ISO 21305/based on ISO 179/1eA
Puncture Impact Behavior - Maximum Force	23 °C	5,200	N	ISO 6603-2
Puncture Impact Behavior - Puncture Energy	23 °C	58	J	ISO 6603-2
Ball Indentation Hardness		128	N/mm²	ISO 2039-1

Electrical properties (23 °C/50 % r. h.)

Property	Test Condition	Value	Unit	Standard
Volume Resistivity		4E17	Ω·m	IEC 62631-3-1
Surface Resistivity		5E16	Ω	IEC 62631-3-2
Electric Strength		31	kV/mm	b.o. IEC 60243-1
Comparative Tracking Index (CTI)	Solution A	600		IEC 60112